摘 要
本研究探討鋁合金板材料，如何滿足航太特殊製程-熱處理規範之驗證，以達到航太供應商供料之資格，而熱處理規範之重點，主要是所使用之熱處理設備、儀器、製程條件、產品檢驗均須實作並符合NADCAP之規範，其主要設備是固溶熱處理爐與時效熱處理爐，其爐具的溫度均勻性(TUS)與系統準確度(SAT)，均須滿足二級爐以上之驗證，且製程與產品須符合航太規範需求。
熱處理爐設施的主要研製流程包括: 1. 確立客戶交貨量與規格需求；2. 設計鋁合金板製造流程； 3. 瞭解熱處理工程之產能狀況；4.達到鋁板固溶熱處理(T4)之目的；5.符合航太熱處理爐具之認證標準； 6. 滿足固溶熱處理爐設施之規範；7.設計滿足固溶熱處理爐規範所需之設施；8. 理解時效熱處理(T6)之目的； 9. 瞭解時效熱處理爐設施之規範；與，10. 設計滿足時效熱處理爐規範所需設施。
除了主要流程外其他相關的品質保證流程與支援流程，亦都須滿足規範要求，且製程参數為最適之條件，才是合格的與較佳的熱處理爐設施。
關鍵字: 固溶熱處理、時效熱處理、溫度均勻性(TUS)、系統準確度(SAT)

Abstract
Key words: solution heat treatment, aging heat treatment, Temperature Uniformity Survey (TUS), System Accuracy Test (SAT)
This thesis aims to design and manufacture a heat-treatment furnance for massively producing aluminum alloy plates that can meet the validation of heat-treatment specificiations to qualify as an aircraft material supplier. The focus of the heat treatment specifications is mainly on the used instruments, process conditions, and product inspections must meet the NADCAP specifications. Its main equipments are a solid solution heat treatment furnace and an aging heat treatment furnace. The temperature uniformity (TUS) and system accuracy test (SAT) of the furnaces must satisfy with all requirements of a Class 2 Furnace and the entire manufacturing processes and products are need to fulfill criteria for aircraft applicaitons.
The process for the development of a qualified heat-treatment furnace is as follows: (1) confirm the requirements of customer delivery and specification; (2) design the manufacturing process for aluminum alloy plate; (3) comprehend capacity status of heat treatment engineering; (4) achieve the purpose of solid solution heat treatment (T4) of aluminum plate; (5) meet the certification standards of heat treatment furnace for aircraft products; (6) meet the requirements of solution heat treatment furnace facilities; (7) design of facilities required to meet solution heat treatment furnace specifications; (8) understand the purpose of aging heat treatment (T6); (9) implement the specifications of aging heat treatment furnace facilities; (10) design facilities meeting all the requirements of an aging heat treatment furnace.
In addition to the main processes, other relevant quality assurance processes and support processes must also meet the requirements of the specification. Besides, the process parameters should be the most suitable conditions, which is the design requirement for a better heat treatment furnace.

參考文獻
[1] 航太扣件熱處理 了解鋁合金熱處理 工業爐技術論壇 Daniel H.Herring.2005.02
[2] 熱處理制度對7075鋁合金顯微組織和性能的影響.材料熱處理技術2008.11
[3] Aerospace material specification pyrometry(2012)
[4] AMS 2750E 高溫量測法 金屬工業研究發展中心 羅萬中2015.10
[5] Aerospace material specification heat treatment of Aluminum alloy
raw material(2016)
[6] ASTM B209-14 Standard Specification for Aluminum and Aluminum-Alloy
Sheet and Plate (2014)
[7] Aerospace material specification Aluminum Alloys 6061/7075 Sheet and
Plate (2014)
[8] Alcqa technical center(2000)
[9] 工程材科學原理與應用 高立圖書出版 李勝隆 2016.06
[10] 熱處理金屬材料原理與應用 全華圖書出版 李勝隆 2014.08
[11]A study on the aging treatment of 6066 and 6061 aluminum alloy
台灣大學材料科學與工程研究所-劉正賢 逢甲大學材料科學與工程研究所-林昆明.2011
[12] 淬火液的選擇及控制 台灣好富頓公司 2013.04
[13] 表面清淨度對7075鋁合金熱處理後之機械性質影響.曹啟彰 2004.05
[14] 熱傳遞學(Heat transfer)高立圖書出版 原著:J.P.Holman 2013.06
[15] The Effects of Solid Solution Treatment on Tensile Properties and Reliability
of Al-Mg-Si Aluminum Alloys.程文宗.2012.08
[16] 南亞技術學院改進教學計劃成果報告-機械材料教學媒體製作.楊慶彬 2008.12
[17] /info.lu.farmingdale.edu/depts./met/met205/agehardening.html
[18] 節約能源技術手冊 經濟部能源局編 2016.12
[19] /www.ndted.org/education resources/community college/eddy currents
[20] Published in:Metallurgical and materials transactions –Boeing (2003)
[21] 解決鋁合金加工變形的方法.新技術新工藝2009.第3期
[22]A Study on precipitation hardening treatment of Al-Zn-Mg-Cu aluminum
alloy 夏汶新 2012.05
[23] 鋁合金金相分析最佳化研究.王約翰 2010.07