以低真空熱蒸鍍冷凝法製備奈米錫微粒，經X 光繞射及AFM 鑑定粒徑為7 nm，從X 光繞射圖及XRF 判定樣品成份皆為錫。在1.8 K 且零外加磁場環境下，測定7 nm 樣品之交流磁化率，結果顯現超導態。
利用壓合的方式以改變樣品微粒間距，討論微粒間的交互作用對超導參數的影響，發現錫塊材的原子距離不是最佳，藉由調控錫的原子距離，使得錫奈米顆粒的臨界溫度大於塊材錫，塊材錫臨界溫度的公認實驗值為3.722K，且超導抗磁效率為塊材的19 倍。邁斯納效應隨微粒間距的減小而增強，其可能之機制是以穿隧距離相關的直流約瑟夫遜效應為主。此外，樣品具有電子自旋極化的現象，自旋極化效應會與超導抗磁性互相競爭，從實驗數據中發現在高壓合密度時，此樣品的超導抗磁性皆大於自旋極化效應。

A set of Sn nanoparticle powder is fabricated by the thermal evaporation method. The mean particle diameter is determined to be 7 nm by X-ray diffraction profiles and AFM images. The zero field ac magnetic susceptibility
measurements reveal that superconductivity occurs below 3.6 K when the particles are very loosely packed.
Interparticle separation is adjusted by a hydraulic press. The effects of interparticle interactions on the superconducting parameters of Sn nanoparticles are investigated. The critical temperature is found to be sensitive to theinterparticle separation a 7% increase in Tc is revealed at a interparticle separation of 2.2 nm. Recalling the interparticle separation results in a
significant increase in the diamagnetism screening effect. As large as 19 times the bulk screening is also observed at an interparticle separation of 0.03 nm.
We found that the inter-atomic distance in the bulk material is not optimized for the forming of superconducting. The origin of enhanced Meissner effect may
be mainly contributed by DC Josephson effect due to reduction of tunneling
distance.

[1] W. H. Li, C. C. Yang, F. C. Tsao, S. Y. Wu, P. J. Huang, M. K. Chung, and Y. D. Yao, Phys. Rev. B. 72, 214516 (2005).
[2] 何均考, 錫奈米微粒的超導參數與自旋極化, 中央大學碩士論文 (2006).
[3] 黃竑杰, 零維銦奈米微粒的超導參數探討, 中央大學碩士論文(2004).
[4] 楊子澔, 鉛奈米微粒的結構分析與超導特性探討, 中央大學碩士論文 (2001).
[5]H. Hori, T. Teranishi, Y. Nakae, Y. Seino, M. Miyake, S. Yamada, Anomalous magnetic polarization effect of Pd and Au nano-particles, Phys. Lett. A 263 406 (1999)
[6] H. Hori, Y. Yamamoto, T. Iwamoto, T. Miura, T. Teranishi, and M. Miyake, Diameter dependence of ferromagnetic spin moment in Au nanocrystals, Phys.
Rev. B 69 174411 (2004)
[7] Y. Yamamoto, T. Miura, M. Suzuki, N. Kawamura, H. Miyagawa, T. Nakamura, K. Kobayashi, T. Teranishi, and H. Hori, Direct Observation of Ferromagnetic Spin Polarization in Gold Nanoparticles, Phys. Rev. Lett 93,
116801 (2004)
[8] S. Y. Wu, and W. H. Li, Observation of magnetic anomalous in Ag nanoparticles (unpublish)
[9] 翁士宇, 微粒間交互作用對奈米錫超導參數的影響, 中央大學碩士論文 (2007).
[10] 陳書偉, 粒子間交互作用對奈米錫自旋極化的增益效應, 中央大學碩士論文 (2007).
[11] W. Meissner and R. Ochsenfeld, Naturewiss, 21, 787 (1933).
[12] 張玉恆、李玉芝著, 超導物理
[13] B.D. Josephson, The discovery of tunneling supercurrents. Rev. Mod. Phys. 1974;46(2):251-254
[14] B.D. Josephson, Coupled superconductors. Rev. Mod. Phys. 36, 216 (1964).
[15] 王進威，擬合X 光繞射峰形判定奈米微粒粉末的粒徑分佈，中央大學碩士論文(2006)
[16] R. Espiau de Lamaestre and H. Bernas, Significance of lognormal nanocrystal size distributions, Phys. Rev. B 73, 125317 (2006)
[17] E. Limpert, W. A. Stahel, and M. Abbt, Log-normal Distributions across the Sciences: Keys and Clues, BioScience 51, 341 (2001)
[18] 陳志瑋，調控鎳奈米微粒粉末的磁化強度，中央大學碩士論
文(2006)
[19]B. D. Cullity, INTRODUCTION TO MAGNETIC MATERIALS.
[20] Steen Mørup and Cathrine Frandsen, Thermoinduced Magnetization in Nanoparticles of Antiferromagnetic Materials, Phys. Rev. Lett 92, 217201 (2004)
[21] D.J.Scalapino and R.Denton,Phys.Rev.B.Vol.6,No.5(1972)
[22] 陳姿蓉，奈米錫顆粒之超導與自旋極化間共存及互競現象，中央大學碩士論文(2007)