由於非對稱壓延可有效降低壓延力及壓延扭矩，使材料於壓延製程安排上，更趨自由與多樣性，在壓延工業之應用上，具有極大之助益；但於非對稱壓延後之板材易產生彎曲現象而造成產品品質降低及設備損壞。
本文以試片厚度2mm及2.9mm的A0150P鋁板進行同徑對稱及非對稱壓延實驗，以探討試片厚度、縮減率、輥輪周速比及界面潤滑條件對成形板材彎曲曲率的效應。實驗結果顯示，(1) 成形試片曲率達到平板狀態理想值(±0.0025)的縮減率和試片厚度成正比關係；(2) 成形試片曲率達到平板狀態理想值(±0.0025)的縮減率和周速比係成正比的關係；(3) 不同界面潤滑條件對於壓延力及壓延扭矩有明顯的降低效應，但對改善成形試片曲率無明顯的效應。

Due to the asymmetrical rolling can reduce rolling force and rolling torque that will make rolling process also flexible and variable. There are extreme advantages in application of rolling industry. The specimens will curvature after the asymmetrical rolling, the flat bending will reduce production quality and impact machine.
This paper observe various of curvature ratio at symmetrical and asymmetrical rolling with different specimens thickness(2mm and 2.9mm),mismatch peripheral speed,reduction, lubrication. The result is that:(1) The specimens reduction that curvature ratio is between ±0.0025 is directly proportional to specimens thickness.(2) The specimens reduction that curvature ratio is between ±0.0025 is directly proportional to mismatch peripheral speed.(3) With Lubrication, rolling force and rolling torque is decreased, but curvature ratio is not improve.

[1] O. Hoffman and G. Sachs, "Introduction to the Theory of Plasticity for Engineers," Fig. 19.1, McGraw-Hill Book Company, New York, 1953.
[2] N. Bay, et al., "Cross Shear Roll Bonding," J. Mater. Process. Technol., 45(1994)1-6.
[3] T. Von Karman, Zeitschrift fur angewandte Mathematik und Mechanik, 5(1925)139.
[4] E. Orowan, "The Calculation of Roll Pressure in Hot and Cold Flat
Rolling," Proceedings of the Institution of Mechanical Engineers, 150(1943) 140-167.
[5] D. R. Bland, and H. Ford, "The Calculation of Roll Force and Torque in Cold Strip Rolling with Tensions," Proc. Instn. Mech. Engrs., 159(1948) 144-153.
[6] H. Ford, F. Ellis, and D. R. Bland, "Cold Rolling with Strip Tension
Part I. A New Approximate Method of Calculation and a Comparison
with Other Method," Jounal of the Iron and Steel Institute, (1951)57-72.
[7] R. B. Sims, "The Calculation of Roll Force and Torque in Hot Rolling
Mills," Proc. Instn. Mech. Engrs., 168(1954)191-200.
[8] J.M. Alexander, "On the Theory of Rolling," Proceedings of the Royal Socity of London. Series A., 326(1972)535-563.
[9] D. Rusia, "Improvements to Alexander''s Computer Model for Force and Torque Calculations in Strip Rolling Process," Journal of the Material
Shaping Technology, 8(1990)167-177.
[10] D. Rusia, "Review and Evaluation of Different Methods for Force and Torque Calculations in the Strip Rolling Process," Journal of the
Material Shaping Technology, 9(1991)117-125.
[11] W. Johnson and G. Needham, "An Experimental Study of
Asymmetrical Rolling," Applied Mechanics Convention, Cambridge,
Instn. Mech. Engrs. 180(1966)270-281.
[12] W. Johnson and G. Needham, "Further Experiments In Asymmetrical rolling", Int. J. Mech. Sci., 8 (February 1966) 433-455.
[13] D. Pan and D. H. Sansome, "An Experimental Study of the Effect of
Roll Speed Mismatch on the Rolling Load during the Cold Rolling of
the Thin strip," Journal of Mechanical Working Technology, 6(1982)361-377.
[14] H. Shiozaki, S. Shinya, M. Mikami, S. Koide. “Experimental Study on the Effects of Differential Roll Speed Ratio on the Rolling Force, Rolling Torque and Forward Slip in Thin Strip Rolling.”, 塑性加工,23(1982)1080-1086
[15] K. Narita et al., "The Characteristics of Curvature in Asymmetrical
Cold Rolling," Proc. s-63 Sp. Conf. of JSTP, (1988)241-244.
[16] J. Jeswiet, P.G.Greene, ”Experimental measurement of curl in rolling,” J. Mater. Proces. Technol., 84(1998)202-209
[17] 黃永茂，徐宏修, "應用流線函數法於壓延加工之研究－單層板非對稱壓延速度場之修正," 第十九屆全國力學會議, (1995)171-178.
[18] H. Dyja, P.Korczak, J.W.Pilarczyk, J. Grzybowski, “Theoretical and Experimental Analysis of Plates Asymmetric Rolling”, Journal of Materials Processing Technology, 45 (1994) 167-172
[19] H. Dyja, J. Markowski and D. Stoninski, “Asymmetry of the Roll Gap as a Factor Improving Work of the Hydraulic Gauge Control in the Plate Rolling Mill”, Journal of Materials Processing Technology, 60 (1996) 73-80.
[20] M.Salimi, F.Sassanib, "Modifed slab analysis of asymmetrical plate
rolling",International Journal of Mechanical Sciences 44 ,
(2002)1999–2023.
[21] A. Kawalek, ”Forming of Band Curvature in Asymmetrical Rolling
Process,”Journal of Materials Processing Technology,155-156(2004) 2033-2038.
[22] A. Kawalek, "The Theoretical and Experimental Analysis of The
Effect of Asymmetrical Rolling on The Value of Unit Pressure," Journal of Materials Processing Technology, 157-158(2004)531-535.
[23] R. Hill, “The Mathematical Theory of Plasticity”, Oxford University Press, London, 1950.
[24] A.T. Male and M.G. Cockcroft, "A Method for the Determination of
the Coefficient of Friction of Metals under Conditions of Bulk Plastic
Deformation", Journal of the Institute of Metals, 93(1964-65)38-46.
[25] Schroeder, W., and Webster, D. A., “Press Forging Thin Sections : Effect of Friction, Area and Thickness on Pressure Required”, Journal of Applied Mechanics, 16(1949)289-294.
[26] J.G. Lenard, “Friction and Forward Slip in Cold Strip Rolling”, Tribology Transactions, 35(1992)423-428.
[27] S. Ekelund, "The Analysis of Fators Influencing Rolling Pressure and Power Consumption in the Hot Rolling of Sheet", Steel, 93(1933)27-29.
[28] R.B. Sims, "The Forward Slip in Cold Strip Rolling", Sheet Metal industries", 29(1952)869-877.
[29] H. Inhaber, "The Coefficient of Friction in Cold Rolling ", Journal of Engineering for Industry, 88(1966)421-429.
[30] W.L. Roberts, "Cold Rolling of Steel", Dekker and Co., New York, (1987).
[31] J. G. Lenard, S. Zhang, “A study of friction during the lubricated cold rolling of an aluminum alloy”, Journal of Materials Processing Technology, 72(1997)293-301.
[32] E.B. Li, A.K. Tieu, W.Y.D. Yuen, “Application of digital image correlation technique to dynamic measurement of the velocity field in the deformation zone in cold rolling”, Optics and Lasers in Engineering, 39(2003)479-488.
[33] A.K. Tieu, Y.J. Liu, “Friction variation in the cold-rolling process”, Tribology International, 37(2004)177-183.
[34] 孟繼洛, “機械材料”, 臺北市:曉園出版社, (1990)430-431
[35] Designation：E8M-91, Standard Test Methods for Tension Testing of
Metallic Materials [Metric], 150-168.
[36] W.F. Hosford and M.C. Caddell, "Metal forming Mechanics and
Metallurgy," Prentice-Hall International, Inc. (1993)55-60.